可膨胀石墨阻燃体系在聚丙烯中的作用

Flame Retardant Effcet of Expandable Graphite on Polypropylene

摘要: 采用可膨胀石墨(EG)为主阻燃剂,包裹红磷(MRP)为阻燃协效剂制备阻燃聚丙烯(PP)。在mEG∶mMRP≥2时,阻燃效果最佳。阻燃剂(FR)含量达到30%后,阻燃效果大幅度提高,氧指数大于28。采用热失重和流变学方法分析了炭层质量,探讨了在mEG∶mMRP≥2时,阻燃效率最高的原因。相容剂马来酸酐接枝聚丙烯(PP-g-MAH)能够改善阻燃剂和聚丙烯之间的相容性,提高粘结力,改善炭层质量,提高材料的氧指数,PP-g-MAH用量为30%时,材料的氧指数达到31.4。

Abstract: The use of expandable graphite(EG) and microcapsulated red phosphorous(MRP) as an intumescent flame-retardant additive in polypropylene was studied using the limiting index(LOI) and the vertical test.The best results appear when ratio of expandable graphi