    Study on the Solution Viscosity Behaviors of Water-Soluble Hydrophobically Associating Copolymers of Acrylamide/Methylacrylaminoethyldimethylalkyl Ammonium Bromide/Sodium Acrylate[J]. Journal of Functional Polymers, 2003, 16(3): 387-391.
    Citation: Study on the Solution Viscosity Behaviors of Water-Soluble Hydrophobically Associating Copolymers of Acrylamide/Methylacrylaminoethyldimethylalkyl Ammonium Bromide/Sodium Acrylate[J]. Journal of Functional Polymers, 2003, 16(3): 387-391.
    shu

    疏水缔合水溶性聚合物AO的溶液粘度行为研究

    Study on the Solution Viscosity Behaviors of Water-Soluble Hydrophobically Associating Copolymers of Acrylamide/Methylacrylaminoethyldimethylalkyl Ammonium Bromide/Sodium Acrylate

      摘要
    • 摘要: 研究了稀溶液中疏水链链长、无机电解质NaCl和CaCl2对疏水缔合水溶性丙烯酰胺／甲基丙烯酰氨乙基-二甲基烷基溴化铵／丙烯酸钠共聚物(AO)在水溶液中的特性粘数和Huggins常数的影响，以及聚合物AO-8的特性粘数和Huggins常数随温度的变化。结果表明：在稀溶液中，无机电解质离子强度增大，共聚物AO在NaCl和CaCl2溶液中的特性粘数减小，Huggins常数增大。在亚浓溶液范围对聚合物质量分数、温度、剪切速率及NaCl含量对聚合物的水溶液表现粘度的影响进行了研究，观察到疏水缔合聚合物盐水溶液在NaCl含量提高的情况下，出现的增粘现象。

       